Marbleizing apparatus

ABSTRACT

Multiple plastisol compositions having differing decorative characteristics are simultaneously individually fed to a receptacle to form a heterogeneous mixture thereof. An applicator ball is positioned in an opening in the receptacle&#39;&#39;s bottom. Rotation of the ball during an oscillating movement of the receptacle, with the ball in contact with a moving substrate, produces a marbleizing effect in the coating applied thereby. Heat is used to gel the marbleized coating. A clear, unfilled plastisol coating is applied over the marbleized coating and the coatings are then heat fused.

11: mi t States Patent 1191 Weaver 1 1 Sept. 17, 11974 1 MARBLEIZING APPARATUS 3,106,480 /1963 Baker 1. 118/221 x 3,155,540 l1/l964 Loeffler et a1. 117/44 X Invent John weavel" Lancaster 3,293,063 12/1966 P01116131 117/39 x 73 Assigneez Armstrong Cork Company, 3,319,601 5/1967 Bal er et a1. 117/43 X Lancaster Pa. 3,461,016 8/1969 lrvmg, Jr. et a1. 425/ 3,479,197 11/1969 Mark 117/45 X [22] Filed: Oct. 110, 1972 [21] APP] 296,109 Primary ExaminerJ. Spencer Overholser Assistant ExaminerRobert J. Craig Related US. Application Data [62] Division of Ser. No. 87,068, Nov. 5, 1970. 57 ABSTRACT 52 us. c1 425/104 117/39 117/45 Multiple P1359801 compositions having differing decol18/259 (/113 2125/22; rative characteristics are simultaneously individually 51 1m. (:1 B 29d 7/00 fed receptacle form hetemgenem mixture [58] Field of Search 425/110 115 113 224 thereof. An applicator ball is positioned in an opening 425/ 131 94 l in the receptacles bottom. Rotation of the ball during 117/39 an oscillating movement of the receptacle, with the ball in contact with a moving substrate, produces a [56] References Cited marbleizing effect in the coating applied thereby. Heat is used to gel the marbleized coating. A clear, unfilled UNITED STATES PATENTS plastisol coating is applied over the marbleized coating :Zeeljet a1. 1 17/39 X d h coatings are h h f d en 1115 3,078,179 2/1963 Kuhn ct al. 118/258 X 5 Claims, 3 Drawing Figures 1 MARBLEIZING APPARATUS CROSS-REFERENCE TO RELATED APPLICATION BACKGROUND OF THE INVENTION 1. Field of the Invention The invention relates to a new method and apparatus for producing a marbleized sheet from a heterogeneous mixture of a combination of vari-colored and uncolored plastisols, and more particularly, to the production of a marbleized sheet by applying the plastisol mixture to a moving substrate by means of a ball positioned in the dispensing opening of a feed receptacle as they are moved with an oscillating motion over the substrate surface.

2. Description of the Prior Art Numerous prior attempts have been made to achieve marbleized or somewhat similar decorative patterns in plastic sheet material. US. Pat. No. 3,219,735, for example, discloses coating of a substrate with a pigmented curable resinous coat; allowing the base coat to set up for a sufficient length of time to form an uncured, but friable film on the surface thereof; application of one or more discontinuous pigmented curable resinous coatings onto the base coat; subjecting the substrate to action to cause the discontinuous coating to slide or flow in relation to the base coating and, allowing the decorative coating to set up and harden.

US. Pat. No. 3,34l ,936, teaches application ofa pigmented base layer ofa curable synthetic resinous liquid coating material to a surface, followed by the application of at least one color pigment of a different color in a random discontinuous pattern overlying the base layer. A substantially transparent layer of the curable resinous liquid coating material is then applied and, before the coating layers have set, the surface of the top layer is acted upon to initiate surface movement only, to induce by wave motion, subsurface flow and diffusion of the pigmented intermediate layer.

US. Pat. Nos. 2,544,622 and 2,615,271 relate to a method and apparatus for forming a patterned pigmented plastic sheet comprising, applying to a support, a thin fluid film of an organic film-forming material which may contain pigment and a solvent and, vibrating the support until the solvent has evaporated and the film solidified.

The formation ofa multi-colored sheeting is also disclosed by US. Pat. No. 3,049,761, wherein granulated resins of various colors are mixed with a plastisol paste and this mixture is formed into a sheet, fused and pressed.

Other prior methods include the dropping of colored plastisol paste onto a solid sheet of resin just before it enters a calender. This squeezes the plastisol paste into the base sheet forming a composite sheet which may have several different colors. The milling together of differently colored pieces of resinous material to form a multi-colored sheet has, of course, also been known.

From the foregoing, it can be seen that some of these prior process involved the application of separate multiple coatings, the necessity of causing shifting, separating, or intermingling, of the coatings and, the loss of time waiting for setting-up, etc. The remaining prior processes above were incapable of producing a controllable and substantially reproducible patterned marbleized sheet such as that of the present invention, which invention further results in an improved marbleized sheet with fewer necessary steps and a saving in time and expense.

SUMMARY OF THE INVENTION The invention herein is directed. to a method and apparatus for producing a marbleized plastic sheet wherein clear, colored and translucent plastisols are simultaneously individually fed to the top surface of a ball which is positioned in the bottom opening ofa feed receptacle. The ball and receptacle are positioned above the surface of a substrate, with the ball in rolling contact therewith. The substrate s. surface may or may not have a release coating thereon depending on whether or not retention of the substrate backing is desired. Movement, preferably oscillating, of the receptacle and ball, and movement of the substrate, thus results in rotation of the ball and deposition thereby of a marbleized plastisol coating on the substrate. The marbleized layer is then heat gelled and an additional coating ofa clear, unfilled, unpigmented plastisol is applied thereover and the two coatings heat fused to form the finished sheet which may be retained on, or stripped from the substrate.

It is therefore an object of this invention to set forth an improved method and apparatus for producing a marbleized plastic sheet wherein a system is provided for programming a wide variety of patterns, each of which is controllable, substantially reproducible and, extends through the thickness of the sheet. Further, the extra steps, time and expense encountered in the prior methods of producing a marbleized sheet are eliminated.

BRIEF DESCRIPTION OF THE DRAWING FIG. 1 is a diagrammatic side elevational view of the apparatus used in the method of this invention; FIG. 11 is a sectional elevational view, partially broken away, of the receptacle, fluid applicator and substrate as they appear in use and, FIG. III is a sectional top plan view of the receptacle with the fluid applicator removed to show the receptacles notched dispensing opening.

DESCRIPTION OF THE PREFERRED EMBODIMENT The marbleized sheet of this invention may be made with apparatus of the type shown in FIGS. I, II, and III of the drawings.

In making themarbleized sheet, multiple streams of plastisol l are fed from supply containers 2 through conduits 3 to a receptacle 4 to form a heterogeneous mixture 5. The amount of plastisol flowing through the conduits 3 may be individually controlled by means of valves 6 therein, to control and influence the character of the marbleized sheet of this invention.

While only one receptacle and attendant apparatus is shown, it will be understood that any number of these assemblies may be mounted across the path of the substrates travel and, that they may be mounted, for example, in parallel, staggered or tandem patterns. It will be further understood such multiple assemblies may be programmed to operate in synchronized and overlapping patterns, all of which may be reproduced within a predetermined cycle.

Each receptacle 4 has a circular opening 7 in its bottom portion, which retains a rotatable, spherical, fluidapplicator 8 which may have a smooth, or a textured surface. The fluid-applicator 8, when not in contact with the substrate 9, rests on the rim 10 of the opening 7. The rim 10 of the opening 7 is preferably serrated as shown in FIG. III at 11 to further facilitate the flow of plastisol and minimize friction between the applicator 8 and the rims edge. In operation, however, with the applicator 8 in contact with substrate 9, receptacle 4 will be spaced above substrate 9 a distance sufficient to allow the applicator 8 to rotate freely in spaced relationship with the rim 10 of the opening 7.

The receptacle 4 may be positioned by means of members 12, resting on cams 13, over a conveyor belt 14 which carries the substrate 9 thereon. Receptacle 4, therefore, may be intermittently raised and lowered by means of members 12 and cams 13 for purposes of achieving desired designed effects. Also, the spacing between the receptacle 4 and the substrate 9 and, the

space between the applicator 8 and the rim 10 of the opening 7 may be varied by means of members 12 and cams 13 while the fluid-applicator 8-is in contact with substrate 9 to regulate the flow of plastisol from the receptacle 4. The substrate 9 may carry a non-adherent coating 15, if it is desired to strip the marbleized sheet from the substrate. However, if it is desired to retain the substrate 9 as a permanent backing, coating 15 may be eliminated and the marbleized sheet secured to the substrate in a known manner.

As conveyor belt 14 is driven by drive means 16, it moves across a conveyor support means 17. Since, in operation the fluid-applicator 8 is in contact with substrate 9, carried on conveyor belt 14, applicator 8 is caused to rotate due to frictional contact therewith. As applicator 8 rotates, it is also caused to move in an oscillating pattern on the surface of substrate 9 by means of cam 18a and roller arrangement 18b. Obviously, the pattern, speed and program, of cam 18a may be varied to produce a wide variety of patterns. As the applicator 8 rotates and is laterally oscillated it carries the partially mixed plastisol 15 onto substrate 9 producing a marbleized coating 19 thereon. The marbleized coating 19 is then gelled by passing it through heating means 20.

The plastisol is preferably fed to receptacle 4 at a rate approximately equal to the rate at which it is being dispensed therefrom. Usually, the amount of plastisol in the receptacle is just enough to cover the applicator. This avoids churning and consequent complete mixing ofthe different colors and results in much better definition of design in the finished product.

A clear, unfilled, unpigmented top coating 21 may then be applied by means of a doctor blade and material supply arrangement such as shown by numeral 22 to level the grained or textured profile of the marbleized coating 19. If it is desired to retain the textured profile of the marbleized coating 19, clear coating 21 may be applied, as by the well-known curtain coating technique in an amount sufficient to only coat the high and low portions and not fill the depressions in the pattern. Coatings l9 and 21 are then fused by heating arrangement 23. The composite sheet 24 may then be stripped from the substrate 9 as by the arrangement 25.

The plastisols used in this invention are made according to well-known methods by mixing resins, plasticizers and stabilizers, coloring materials and other compounding ingredients as desired.

Although the invention is directed primarily to the use of polyvinyl chloride plastisol dispersions, it will be obvious that other alternate resin systems may be used. These would include, for example, polystyrene, polyethylene, polyacrylates, polyvinylidene chloride, polypropylene, polyesters, polyimides, silicones, cellulosics, acrylonitrile-butadiene-styrene, polyurethane and, epoxy.

The temperatures employed with the foregoing synthetic resin materials which may be used in this invention will depend upon the properties thereof and the plasticizers and solvents used therewith, as well understood in the art.

For any given mixture there will be a maximum and a minimum sheet thickness obtainable. Thicknesses between these limits can be obtained by proper selection of ranges, sizes, amounts, etc. of the previously stated factors involved.

The clear and colored plastisols used in this invention are preferably viscous liquids with a consistency some-. what similar to that of toothpaste. Each receptacle may contain a different color or combination of colors, clear or translucent plastisol.

The character of the marble pattern of the plastic sheet formed by this invention was found to be a function of several factors, including:

1. Viscosity of the plastisol.

2. Clearance of the ball above the receptacle socket.

3. Size, density and surface geometry of the ball.

4. Speed of travel of the ball on the substrate or movement of the substrate under the ball.

5. Lateral and/or vertical pattern followed by the ball and receptacle as it traverses the sheet.

6. Height of the plastisol in the receptacle.

Since the plastisol mixture 5 is substantially at heterogeneous one and, is rolled onto substrate 9 by applicator 8 in that condition, a former pattern may be substantially reproduced by controlling the colors of plastisol streams 1 and the rates of flow thereof, together with control of items 1 to 6 above.

As previously stated, it has also been found that improved pattern control and definition may be obtained by providing a notched surface 11 on the rim 10 of the opening 7 of the receptacle 4 as shown in FIG. III. This prevents a build-up of blended plastisol color in the bottom of the receptacle 4, and reduces the scraping action of the openings rim on the ball.

The invention is further illustrated by forming a plastic marbleized sheet using clear, colored and translucent plastisols prepared according to the following formulations. All percentages are by weight unless other wise specified.

I. A 30 percent filled, unpigmented translucent plastisol was formed as follows:

Polyvinyl chloride resin 50.04%

2-2-4 Trimcthyl l-3 pentane diol monoisobutyrate benzoate l l.6l71

2-2-4 Trimethyl l-3 pentane diol diisobutyrate 4.01%

-Continued Epoxy octyl tallate 1 1 Bariurn-zinc phenate, cadmium octoate diphenyl decyl phosphite 1.43%

Calcium carbonate powder 30.00%

Submicroscopic silicon dioxide l.30 100.0071

II. A pigmented plastisol was formed by adding a color dispersion consisting of 40 percent to 70 percent color in di(2-ethyl hexyl) phthalate. Two percent of this color dispersion was added to 98 percent of the formula of Roman Numeral I above.

III. A clear, unfilled unpigmented plastisol was formed as follows:

Polyvinyl chloride resin The formulations ofl and ll above were used to form a fluid marbleized coating on a substrate by applying the plastisols to the substrate in the manner previously described. This coating was then heat gelled. A top coating using formula Ill above was then applied to level the grained profile of the marbleized coating, after which, the coatings were fused by heat and the composite sheet was stripped from the substrate. A very good marbleized pattern sheet was obtained with the pattern extending clear through the thickness ofthe sheet.

The viscosity ranges for the above three plastisols were:

I. 30 percent filled, unpigmented translucent plastisol l,000 30,000 centipoises.

II. I above with 2 percent with color dispersion (40 percent to 70 percent) in di-Z-ethyl hexyl phthalate l,000 to 30,000 centipoises.

lll. Clear, unfilled, unpigmented plastisol 500 2,000 centipoises.

The foregoing example illustrates but one of the many possible variations and materials, methods of application and treatment which may be useful in carrying out the invention.

Since natural marbles and like natural stone materials appear in almost infinite variety of colors and patterns, the invention is unlimited by either the colors which are employed or the patterns in which they are arranged. Obviously, the marbleizing plastisols could be individually applied as well as mixed and applied together as a heterogeneous mixture. It is also obvious that multiple receptacle and ball applicators could be used and that various movements could be imparted to the substrate as well as the applicators to achieve the desired patterns.

What is claimed is:

1. An apparatus for producing a controlled and substantially reproducible marbleized plastic sheet material comprising:

1. at least one receptacle for receiving and dispensing plastisol compositions,

2. fluid access means in the upper portion of said receptacle and a dispensing opening in the bottom thereof,

3. rotatable ball-shaped fluid-applicating means positioned in the bottom opening in said receptacle,

4. means for feeding a plurality of streams of plastisols having differing decorative characteristics to said receptacle to form a heterogeneous mixture thereof,

5. a movable support means adapted to carry a substrate having a non-adherent top surface,

6. means for mounting said receptacle above said substrate and its support means with said fluidapplicating means adapted to be moved into and out of contact with the substrate,

7. means for moving said fluid-applicating means into and out of contact with said substrate,

8. means for moving the substrate which thereby rotates the fluid-applicating means when in contact therewith,

9. means for moving the fluid-applicating means in an irregular pattern on the surface of said substrate to form a marbleized coating thereon,

10. means for gelling the marbleized coating,

11. means for applying a clear plastisol coating over said marbleized coating,

12. means for fusing the marbleized and clear plastisol coatings, and

13. means for stripping the resulting clear coated, marbleized composite sheet from the non-adherent surface of the substrate.

2. An apparatus according to claim 1, wherein, the dispensing opening has a rim and the rim of the dispensing opening in the bottom of the receptacle is serrated to minimize contact of the applicator therewith and facilitate flow of the plastisol therefrom.

3. An apparatus according to claim 1, wherein, the fluid-applicating means rests in the dispensing opening in the receptacle, and floats freely within the opening while being rotated by movement of the receptacle and the substrate.

4. An apparatus according to claim 1, including means for spacing said receptacle above said substrate when said fluid-applicating means is in contact with the substrate, a distance sufficient to cause a spaced relationship between the fluid-applicating means and the dispensing opening in the receptacle to facilitate the flow of the plastisol therefrom.

5. An apparatus according to claim 1, including means for moving said fluid-applicating means intermittently into and out of contact with said substrate. 

1. An apparatus for producing a controlled and substantially reproducible marbleized plastic sheet material comprising:
 1. at least one receptacle for receiving and dispensing plastisol compositions,
 2. fluid access means in the upper portion of said receptacle and a dispensing opening in the bottom thereof,
 3. rotatable ball-shaped fluid-applicating means positioned in the bottom opening in said receptacle,
 4. means for feeding a plurality of streams of plastisols having differing decorative characteristics to said receptacle to form a heterogeneous mixture thereof,
 5. a movable support means adapted to carry a substrate having a non-adherent top surface,
 6. means for mounting said receptacle above said substrate and its support means with said fluid-applicating means adapted to be moved into and out of contact with the substrate,
 7. means for moving said fluid-applicating means into and out of contact with said substrate,
 8. means for moving the substrate which thereby rotates the fluid-applicating means when in contact therewith,
 9. means for moving the fluid-applicating means in an irregular pattern on the surface of said substrate to form a marbleized coating thereon,
 10. means for gelling the marbleized coating,
 11. means for applying a clear plastisol coating over said marbleized coating,
 12. means for fusing the marbleized and clear plastisol coatings, and
 13. means for stripping the resulting clear coated, marbleized composite sheet from the non-adherent surface of the substrate.
 2. fluid access means in the upper portion of said receptacle and a dispensing opening in the bottom thereof,
 2. An apparatus according to claim 1, wherein, the dispensing opening has a rim and the rim of the dispensing opening in the bottom of the receptacle is serrated to minimize contact of the applicator therewith and facilitate flow of the plastisol therefrom.
 3. An apparatus according to claim 1, wherein, the fluid-applicating means rests in the dispensing opening in the receptacle, and floats freely within the opening while being rotated by movement of the receptacle and the substrate.
 3. rotatable ball-shaped fluid-applicating means positioned in the bottom opening in said receptacle,
 4. means for feeding a plurality of streams of plastisols having differing decorative characteristics to said receptacle to form a heterogeneous mixture thereof,
 4. An apparatus according to claim 1, including means for spacing said receptacle above said substrate when said fluid-applicating means is in contact with the substrate, a distance sufficient to cause a spaced relationship between the fluid-applicating means and the dispensing opening in the receptacle to facilitate the flow of the plastisol therefrom.
 5. An apparatus according to claim 1, including means for moving said fluid-applicating means intermittently into and out of contact with said substrate.
 5. a movable support means adapted to carry a substrate having a non-adherent top surface,
 6. means for mounting said receptacle above said substrate and its support means with said fluid-applicating means adapted to be moved into and out of contact with the substrate,
 7. means for moving said fluid-applicating means into and out of contact with said substrate,
 8. means for moving the substrate which thereby rotates the fluid-applicating means when in contact therewith,
 9. means for moving the fluid-applicating means in an irregular pattern on the surface of said substrate to form a marbleized coating thereon,
 10. means for gelling the marbleized coating,
 11. means for applying a clear plastisol coating over said marbleized coating,
 12. means for fusing the marbleized and clear plastisol coatings, and
 13. means for stripping the resulting clear coated, marbleized composite sheet from the non-adherent surface of the substrate. 